Polyester film with finely textured structure on the front side suitable for window printing with UV lacquers. Reverse side with ink receptive coating. Material is available with a thickness of 0.13 mm.
GO-FT is available either in sheets or reels. The maximum sheet or reel width is 610 mm.
All sheets are equipped with interleaving paper as standard.
GO–FT is a discontinued product and has been replaced by the new GO–FT NQ with UV protection available in 122cm width.
|Art. Number||Nominal thickness (mm)||Packing quantity|
|Art. Number||Length (m)||Nominal thickness (mm)|
- Ink receptive coating
- Suitable for window printing
|Haze||ASTM D1003-77||50 - 65%|
|Gloss level (60°)||ASTM D2457-70, ASTM D523||17 - 24 GU|
|Tensile strength at break||ASTM D 882||170 N/mm2|
|Switch life||Folex method according to DIN 42115||> 5 Mio. flexes|
|Chemical stability||Folex method||good|
|Dielectric strength1||ASTM D149-81||120 kV/mm (125 µm)|
|Shrinkage TD||130°C 30 min Folex method||< 0,7%|
|Shrinkage MD||130°C 30 min Folex method||< 1,0%|
|Maximum processing temperature||120°C|
|Melting temperature1||ASTM E794-85||255°C|
|Roughness Ra||EN ISO 4287, ASME B46.1||1,3 - 2,0 µm|
|Scratch resistance||Folex method||good|
|Surface tension front side||DIN 53364, ASTM D2578||48-54 mN/m|
|Surface tension reverse side||DIN 53364, ASTM D2578||35 - 41 mN/m|
1 Data derived from base film Polyester manufacturer's literature
|Nominal thickness (mil)||5.2|
|Nominal thickness (mm)||0.13|
- Suitable for Membrane Switches, sign production as well as for production of labels
- Preliminary testing necessary by customer
- Once packaging is opened, store at a room temperature of 15 - 25°C and at a humidity of 30 - 60 %
- Shelf life 1 year after delivery (under above storage conditions)