Tack S WO

White polypropylene adherent film with grey back and polyester release liner. Suitable for labels, posters, displays, shop and exhibition panels, on panels of rigid foam, varnished surfaces, metal, glass and light structured surfaces.

Printing Systems



Rolls

Art. NumberWidth (mm)ThicknessLength (m)
22TC0.120.359006100.190 mm20PDF
22TC0.120.3200012700.190 mm20PDF

Technical data

Characteristic

  • High brillance of colours
  • High opacity
  • Can be laminated right to the edges
  • Adhesive light
  • Universal use
  • Removable

Finish

  • White, satin

Specifications

Release linersilicone PET-film
Coating Printsidewhite, satin
Coating Backsidegreyback
Width (mm)610
Core Diameter76 mm
Type of adhesiveEVA adherent layer
Length (m)20
Adhesive coating 0.190 mm
Base Materialpolypropylene multilayer extruded cast film
Total thickness0.220 mm
Packing quantity 1 roll

Compatibility

  • Useable on most large format Ink Jet printers using solvent ink systems.

Handling

Hints:

not suited for application on surfaces containing plasticised PVC, because the active component of the adhesive connects permanently with the mentioned substrate and therefore a removing turns very difficult. Furthermore Tack S WO is very difficult to remove from plastic material such as PE or PP when the surfaces have been pre-treated with chemicals or Corona.

 

In case of further processing with other printing technologies Tack S WO can be printed with normally drying and UV curable offset printing inks.
Following Michael Huber’s inks / Munich have been tested to this end:
Normally drying inks:

RESISTA Label N5080, with dampening additives HYDROFIX B 8013
UV curable:

UV Serie NewV Poly UP5000, with dampening additives NewV fix 8015
For more details on the printing inks, please contact the manufacturer directly.


  • Note for temperature setting: Before printing you must check that the correct drying temperature has been set by carrying out a trial print. Too high drying temperatures can lead to a deformation of the film which can later cause further problems while processing.
  • Note for Drying time / Processing: The VOC which are contained in solvent and latex inks must be fully dried before further processing. For this reason it is necessary to take long enough drying times into account. The drying time of the printed media depends very much on the quantity of solvent applied. When printing the film in a roll-to-roll process, the printed strip must be unrolled and laid flat as soon as possible until final drying. Solvent residues due to insufficient drying times can lead to blocking during transport in rolled-up form. During lamination such residues can negatively impact the quality of the finished product (flatness, shrinkage behaviour, anchorage, etc...).
  • It is necessary to protect the surface if it is subject over a long time to abrasion or any other mechanical influences, to dirt or humidity. The lamination can be done right to the edges or over the edges. The user should check before using what is more appropriate.
  • We recommend to use self-adhesive laminating foils for cold lamination.

Storage

  • After printing the remaining roll must be removed from the plotter and stored in its closed original packing in a cool and dry environment.