Clear glossy self-adhesive PVC film with paper backing. Suitable for labels, posters, displays and exhibition panels. SIVK is also suitable for glass decoration and shop window graphic advertising or as backlit applied directly on light diffusion boards.

Printing Systems



Rolls

Art. NumberWidth (mm)ThicknessLength (m)
22VK0.100.340004300.110 mm20PDF
22VK0.100.359006100.110 mm20PDF
22VK0.100.390009140.110 mm20PDF
22VK0.100.3050010670.110 mm20PDF
22VK0.100.3200012700.110 mm20PDF
22VK0.100.3330013700.110 mm20PDF

Technical data

Characteristic

  • High brillance of colours
  • Adhesive light
  • Universal use

Finish

  • Clear glossy
  • self-adhesive with paper backing

Specifications

Release linersiliconized paper ~ 0.145 mm
Coating PrintsidePower-Gloss®, clear glossy
Width (mm)430
Thickness base material with inkjet coating0.110 mm
Core Diameter50 mm
Adhesion strength~ 7.5.N / 25 mm (A.F.E.R.A.), after 24 h ~ 10 N / 25 mm (A.F.E.R.A.)
Type of adhesivepolyacrylate dispersion, semipermanent
Length (m)20
Base Materialcalendered monomeric plasticized PVC, 0.100 mm
Total thickness0.260 mm
Packing quantity 1 roll

Compatibility

  • Suitable for most Ink Jet plotters using dye- or pigmented inks

Handling

  • Laminating: The printed surface must be protected with foils for cold lamination if it is subject to humidity, sweaty hands, abrasion or any other influences. For a short term outdoor use, SIVK must always be protected with a 5mm overlapping lamination.
  • Gluing: SIVK will stick to any solid, smooth surfaces which are dry and free of dirt, grease, silicon etc. Before gluing it is absolutely necessary to check that the surface is appropriate to this aim and that it has been prepared (cleaned) professionally. During gluing the temperature must reach at least 15°C. You can remove SIVK by heating the film’s surface with a hot air gun. Then pull it off carefully.