Menu

Textured Film

GO-FT

Polyester film with finely textured structure on the front side suitable for window printing with UV lacquers. Reverse side with ink receptive coating. Material is available with a thickness of 0.13 mm.

GO-FT is available either in sheets or reels. The maximum sheet or reel width is 610 mm.

All sheets are equipped with interleaving paper as standard.

GO–FT is a discontinued product and has been replaced by the new GO–FT NQ with UV protection available in 122cm width.

Cut sheets

Art. NumberNominal thickness (mm)Packing quantity
48164.130.xxxxx0.13100PDF

Rolls

Art. NumberLength (m)Nominal thickness (mm)
48164.130.xxxxx1000.13PDF

Technical data

Characteristic

  • Ink receptive coating
  • Suitable for window printing

Properties

PropertyTestmethodValue
Optical
HazeASTM D1003-7750 - 65%
Gloss level (60°)ASTM D2457-70, ASTM D52317 - 24 GU
Mechanical
EmbossingFolex methodpossible
Tensile strength at breakASTM D 882170 N/mm2
Switch lifeFolex method according to DIN 42115 > 5 Mio. flexes
Chemical
Chemical stabilityFolex methodgood
Electrical
Dielectric strength1ASTM D149-81120 kV/mm (125 µm)
Thermal
Shrinkage TD130°C 30 min Folex method< 0,7%
Shrinkage MD130°C 30 min Folex method< 1,0%
Maximum processing temperature120°C
Melting temperature1ASTM E794-85255°C
Surface
Roughness RaEN ISO 4287, ASME B46.11,3 - 2,0 µm
Scratch resistanceFolex methodgood
Surface tension front sideDIN 53364, ASTM D257848-54 mN/m
Surface tension reverse sideDIN 53364, ASTM D257835 - 41 mN/m

1 Data derived from base film Polyester manufacturer's literature

Specifications

Nominal thickness (mil)5.2
Nominal thickness (mm)0.13
Base MaterialPolyester
Packing quantity 100

Product Applications

  • Suitable for Membrane Switches, sign production as well as for production of labels

Handling

  • Preliminary testing necessary by customer

Storage

  • Once packaging is opened, store at a room temperature of 15 - 25°C and at a humidity of 30 - 60 %
  • Shelf life 1 year after delivery (under above storage conditions)

Downloads (PDF)