Anti Reflective Films

GO-AG/AN

Polyester film with anti glare coating on the front side. Reverse side with ink receptive coating and micro rough surface to avoid Newton rings. High-UV and outdoor stability. Material is available with a thicknesses of 0.13 mm and 0.18 mm.

Available in sheets and rolls. Sheets available in standard packing unit or on demand. All sheets are equipped with interleaving paper as standard.

Cut sheets

Art. NumberNominal thickness (mm)Packing quantity
48204.130.xxxxx0.13100PDF
48204.180.xxxxx0.18100PDF

Rolls

Art. NumberLength (m)Nominal thickness (mm)
48204.130.xxxxx1000.13PDF
48204.180.xxxxx1000.18PDF

Technical data

Characteristic

  • Ink receptive coating
  • Suitable for window printing
  • Suitable for textured laquers
  • With UV protection

Properties

Propertiestest methodValue
Optical
HazeASTM D1003-7720 - 35%
Gloss level (60°)ASTM D2457-70, ASTM D52345 - 65 GU
Mechanical
EmbossingFolex methodpossible
Tensile strength at breakASTM D 882170 N/mm2
Switch lifeFolex method according to DIN 42115 > 5 Mio. flexes
Chemical
Chemical stabilityFolex methodgood
Electrical
Dielectric strength1ASTM D149-81120 kV/mm (125 µm)
Thermal
Shrinkage TD130°C 30 min Folex method< 0,7%
Shrinkage MD130°C 30 min Folex method< 0,7%
Maximum processing temperature120°C
Melting temperature1ASTM E794-85255°C
Surface
Roughness RaEN ISO 4287, ASME B46.10,7 - 1,1 µm
Scratch resistanceFolex methodgood
Surface tension front sideDIN 53364, ASTM D257828 - 35 mN/m
Surface tension reverse sideDIN 53364, ASTM D257844 ± 2 mN/m

1 Data derived from base film Polyester manufacturer's literature

Specifications

Nominal thickness (mil)5.2
Nominal thickness (mm)0.13
Base MaterialPolyester
Packing quantity 100

Product Applications

  • Suitable for Membrane Switches, sign production as well as for production of labels

Handling

  • Preliminary testing necessary by customer

Storage

  • Once packaging is opened, store at a room temperature of 15 - 25°C and at a humidity of 30 - 60 %
  • Shelf life 1 year after delivery (under above storage conditions)

Downloads (PDF)