Clear Films

GO-HC

Scratch resistant polyester film with clear coating on the front side suitable for structured printing with UV lacquers. The reverse side has an ink receptive coating.

Material is available with a thickness of 0.13 mm and 0.18 mm. Available in sheets and rolls. Sheets available in standard packing unit or on demand. All sheets and rolls are equipped with self-adhesive protective film on the reverse side as standard.

Cut sheets

Art. NumberNominal thickness (mm)Packing quantity
45411.130.xxxxx0.13100PDF
45411.180.xxxxx0.18100PDF

Rolls

Art. NumberLength (m)Nominal thickness (mm)
45411.130.xxxxx1000.13PDF
45411.180.xxxxx1000.18PDF

Technical data

Characteristic

  • Ink receptive coating
  • Suitable for textured laquers

Properties

PropertiesTest MethodValue
Optical
HazeASTM D1003-77*0,3 - 1,5%
Gloss level (60°)ASTM D2457-70, ASTM D523135 - 145 (20°) GU
Total luminous transmissionASTM D1003-77*88 - 94%
Mechanical
EmbossingFolex methodpossible
Tensile strength at breakASTM D 882170 N/mm2
Switch lifeFolex method according to DIN 42115> 5 Mio. flexes
Chemical
Chemical stabilityFolex methodvery good
Thermisch
Shrinkage TD130°C 30 min Folex method< 0,5%
Shrinkage MD130°C 30 min Folex method< 1,0%
Maximum processing temperature120°C
Melting temperature1ASTM E794-85255°C
Surface
Roughness RaEN ISO 4287, ASME B46.10,04 - 0,4 µm
Surface hardnessFolex method3 H
Scratch resistanceFolex method very good
Surface tension front sideDIN 53364, ASTM D257835 - 38 mN/m
Surface tension reverse sideDIN 53364, ASTM D257838 ± 2 mN/m

1 Data derived from base film Polyester manufacturer's literature

Specifications

Nominal thickness (mil)5.2
Nominal thickness (mm)0.13
Base MaterialPolyester
Packing quantity 100

Product Applications

  • Suitable for Membrane Switches, sign production as well as for production of labels

Storage

  • Once packaging is opened, store at a room temperature of 15 - 25°C and at a humidity of 30 - 60 %
  • Shelf life 1 year after delivery (under above storage conditions)