GO-CL VP

Clear Polyester film with double sided ink receptive coating. Material is available with thicknesses of 0.13 mm, 0.18 mm and 0.25 mm. Available in sheets and rolls. Sheets available in standard packing unit or on demand. All sheets are equipped with interleaving paper as standard. Options such as self-adhesive protective film is available but will be an additional cost.

Cut sheets

Art. NumberNominal thickness (mm)Packing quantity
4813x.130.xxxxx0.13100PDF
4813x.180.xxxxx0.18100PDF
4813x.250.xxxxx0.25100PDF

Rolls

Art. NumberLength (m)Nominal thickness (mm)
4813x.130.xxxxx1000.13PDF
4813x.180.xxxxx1000.18PDF
4813x.250.xxxxx1000.25PDF

Technical data

Characteristic

  • Ink receptive coating
  • Suitable for textured laquers

Finish

  • Clear

Properties

PropertyTest MethodValue
Optical
HazeASTM D1003-77< 1%
Total luminous transmissionASTM D1003-77> 90%
Mechanical
EmbossingFolex methodpossible
Tensile strength at breakASTM D 882170 N/mm2
Switch lifeFolex method according to DIN 42115> 5 Mio. flexes
Chemical
Chemical stabilityFolex methodpartly resistant
Electrical
Dielectric strength1ASTM D149-81120 kV/mm (125 µm)
Thermal
Shrinkage TD130°C 30 min Folex method< 1,0%
Shrinkage MD130°C 30 min Folex method< 1,0%
Maximum processing temperature120°C
Melting temperature1ASTM E794-85255°C
Surface
Roughness RaEN ISO 4287, ASME B46.10,2 - 0,4 µm
Scratch resistanceFolex methodpartly resistant
Surface tension front sideDIN 53364, ASTM D257838 - 41 mN/m
Surface tension reverse sideDIN 53364, ASTM D257838 - 41 mN/m

1 Data derived from base film Polyester manufacturer's literature

Specifications

Nominal thickness (mil)5.2
Nominal thickness (mm)0.13
Base MaterialPolyester
Packing quantity 100

Product Applications

  • Suitable for Membrane Switches, sign production as well as for production of labels

Handling

  • Preliminary testing necessary by customer

Storage

  • Once packaging is opened, store at a room temperature of 15 - 25°C and at a humidity of 30 - 60 %
  • Shelf life 1 year after delivery (under above storage conditions)